SAE AS 81044-13-2000 pdf download WIRE, ELECTRIC, CROSSLINKED POLYALKENE INSULATED, SILVER-COATED HIGH STRENGTH COPPER ALLOY, LIGHT WEIGHT, 600-VOLT, 1 50°C
TEMPERATURE RATING: 150C (302F) MAX CONDUCTOR TEMPERATURE
VOLTAGE RATING: 600 VOLTS (RMS) AT SEA LEVEL
ACCELERATED AGING: OVEN TEMPERATURE, 300 2C (572 3.6) FOR 6 HOURS; FOR DENTIFICATIONLEGIBILITY,225 2C(437 3.6F)FOR 6 HOURS
BLOCKING: 225 2C(437 3.6F)
COLOR: IN ACCORDANCE WITH MIL-STD-104.CLASS 1: WHITE PREFERRED
FLAMMABILITY: 30 SECONDS (MAX); 3.0 INCHES (MAX) NO FLAMING OF TISSUE PAPER
HUMIDITY RESISTANCE: 5000 MEGOHMS FOR 1000 FT,MIN INSULATION RESISTANCE AFTER HUMIDITYEXPOSURE
IDENTIFICATION OF PRODUCT: NOT REQUIRED ON SIZES 28 OR 30
IDENTIFICATION,STRIPINGOR BANDING DURABILITY: 125 CYCLES (250 STROKES)(MIN), 500 GRAMS WEIGHT
IMPULSE DIELECTRIC TEST:
PRIMARY INSULATION (WHEN TEST IS USED IN LIEU OF SPARK TEST: 6.0 KILOVOLTS PEAK), 100% TESFINISHED WIRE: 8.0 KILOVOLTS(PEAK),100% TEST
INSULATION RESISTANCE: 5000 MEGOHMS FOR 1000 FT (MIN)LIFE CYCLE: OVEN TEMPERATURE200 2C (392 +3.6F)FOR 168 HOURSPHYSICAL PROPERTIES OF PRIMARY INSULATION:
TENSILE STRENGTH,2500 PSI(MIN)
ELONGATION，150%(MIN)
POLYIMIDE CURE TEST: NOT APPLICABLE
PROPELLANT RESISTANCE: TEST REQUIRED
SHRINKAGE: 0.125INCH MAX AT 300 2C(572 3.6F)
SMOKE: 200 2°C(392 3.6F)
SPARK TEST OF PRIMARY INSULATION: 3000 VOLTS (RMS),60Hz,100% TESTSURFACE RESISTANCE: 500 MEGOHMS-INCHES (MIN),INITIAL AND FINAL READINGS
THERMAL SHOCK:OVEN TEMPERATURE，150 2C(302 3.6F)
MAX CHANGE IN MEASUREMENT: 0.060 INCH
WET DIELECTRIC TEST: 2500 VOLTS (RMS)
WICKING: 2.25 INCHES(MAX)
WRAP TEST: MANDREL WRAP TEST REQUIRED
SAE AS 81044-13-2000 pdf download
PS:Thank you for your support!