SAE AS 81044-11-2000 pdf download WIRE, ELECTRIC, CROSSLINKED POLYALKENE INSULATED, SILVER-COATED COPPER, LIGHT WEIGHT, 600-VOLT, 1 50°C
WIRE RATINGS AND ADDITIONAL REQUIREMENTS
TEMPERATURE RATING: 150C(302F) max conductor temperature
VOLTAGE RATING: 600 volts (rms) at sea level
ACCELERATED AGING: Oven temperature, 300 +2°C (572 +3.6″F) for 6 hours; for identification legibility, 225 +2”C(437 +3.6F)for 6 hours
BLOCKING: 225 2C(437 3.6F)
COLOR: In accordance with MIL-STD-104,Class 1: white preferred
FLAMMABILITY: 30 seconds (max); 3.0 inches (max); no flaming of tissue paperHUMIDITY RESISTANCE: 5000 megohms for 1000 ft, min insulation resistance after humidity exposureIDENTIFICATION OF PRODUCT: Not required on sizes 28 or 30
IDENTIFICATION, STRIPING,OR BANDING DURABILITY: 125 cycles (250 strokes) (min), 500 grams weight
IMPULSE DIELECTRIC TEST:
Primary insulation (when test is used in lieu of spark test): 6.0 kilovolts (peak), 100% testFinished wire: 8.0 kilovolts (peak), 100% test
INSULATION RESISTANCE: 5000 megohms for 1000 ft (min)
LIFE CYCLE: Oven temperature, 200 +2″C(392 3.6F) for 168 hours
PHYSICAL PROPERTIES OF PRIMARY INSULATION:Tensile strength, 2500 psi (min)
Elongation,150%(min)
POLYIMIDE CURE TEST: Not applicable
PROPELLANT RESISTANCE: Test required
SHRINKAGE: 0.125 inch max at 300 2C(572 3.6F)
SMOKE: 200 +2C1392 3.6%F)
SPARK TEST OF PRIMARY INSULATION: 1500 volts (rms),60Hz,100% test
SURFACE RESISTANCE: 500 megohmsinches (min),initial and final readings
THERMAL SHOCK:
Oven temperature 150 2C(302 3.6FMax change in measurement: 0.060 inch
WET DIELECTRIC TEST: 2500 volts (rms)
WICKING: 2.25 inches (max)
WRAP TEST: Mandrel wrap test required