SAE AS 22759-46-2000 pdf download WIRE, ELECTRICAL, FLUOROPOLYMER-INSULATED, CROSS- LINKED MODIFIED ETFE, LIGHTWEIGHT, NICKEL-COATED HIGH-STRENGTH COPPER ALLOY, 200°C, 600 VOLT
RATINGS:
Temperature rating: 200°C (392°F) maximum continuous conductor temperature.
Voltage rating: 600 volts (rms) at sea level.
ADDITIONAL REQUIREMENTS:
Acid resistance: No requirement.
Blocking: 230°C ±3°C (446°F ±5.4°F).
Color: In accordance with MIL-STD-1 04, class 1 ; white preferred. Conformity of color to the limits of MIL-STD-1 04 shall not be required after crosslinking proof test or life cycle oven exposure.
Color striping or banding durability: 1 25 cycles (250 strokes) (min), 500 grams weight.
Crosslinking proof test: 7 hours at 300°C ±3°C (572°F ±5.4°F). Quality conformance test, group II. Requirements and procedures as for life cycle except for time and temperature.
Dielectric test after immersion: 2,500 volts (rms), 60 Hz.
Flammability: Quality conformance test, group II. For requirements and procedures see below.
Humidity resistance: After humidity exposure, wire shall meet the requirements for initial insulation resistance.
Identification of product: Not required for size 24 and smaller. Color code designator not required.
Identification durability: 1 25 cycles (250 strokes) (min), 500 grams weight.
Immersion: For procedure see below.
Impulse dielectric test: 8.0 kilovolts (peak), 1 00 percent test.
Insulation resistance, initial: 5,000 megohms for 1 ,000 feet (min).
Insulation thickness: 0.005 inch (min).
Life cycle: 500 hours at 230°C ±3°C (446°F ±5.4°F). Dielectric test, 2,500 volts (rms), 60 Hz. Procedure to use mandrels coated with polytetrafluoroethylene in the form of either enamel or wrapped tape, such that the diameter of the mandrels,after coating, still conform to the requirements of performance details, table II.
SAE AS 22759-46-2000 pdf download