SAE AS 22759-3-2000 pdf download WIRE, ELECTRIC, FLUOROPOLYMER-INSULATED, TFE-GLASS-TFE, MEDIUM WEIGHT, NICKEL-COATED COPPER CONDUCTOR, 600-VOLT
TEMPERATURE RATING: 260°C (500°F) max conductor temperature
VOLTAGE RATING: 600 volts (rms) at sea level
SPARK TEST OF PRIMARY INSULATION: Not required
IMPULSE DIELECTRIC TEST: 8.0 kilovolts (peak), 1 00% test
INSULATION RESISTANCE: 5000 megohms for 1 000 ft (min)
WRAP TEST:
Mandrel wrap test required; no cracking
Dielectric test after mandrel wrap, 2500 volts (rms), 60Hz
BLOCKING: 260 ±2°C (500 ±3.6°F)
SHRINKAGE: 0.1 25 inch max at 260 ±2°C (500 ±3,6°F)
WICKING:
Sizes 22 through 1 2 – Procedure II; 2.0% (max) weight increase, 0.250 inch (max) dye travel
Sizes 1 0 through 00 – No requirement
LOW TEMPERATURE (COLD BEND):
Bend temperature: -65 ±2°C (-85 ±3.6°F)
Dielectric test, 2500 volts (rms), 60Hz
THERMAL SHOCK:
Oven temperature, 260 ±2°C (500 ±3.6°F)
Max change in measurement
Sizes 22 through 1 2: 0.060 inch
Sizes 1 0 through 8: 0.1 00 inch
Sizes 6 through 00: 0.1 25 inch
FLAMMABILITY: Post-flame dielectric test not required
LIFE CYCLE:
Oven temperature 31 3 ±2°C (595.4 ±3.6°F)
Dielectric test, 2500 volts (rms), 60Hz
DIELECTRIC TEST AFTER IMMERSION: 2500 volts (rms), 60Hz
ABRASION RESISTANCE AFTER IMMERSION: Qualification test only
HUMIDITY RESISTANCE: 5000 megohms for 1 000 ft, min insulation resistance after humidity exposure SURFACE RESISTANCE:
Sizes 22 through 1 2: 500 megohm-inches (min), initial and final readings
Sizes 1 0 through 00: No requirement
SMOKE: 31 3°C (595.4°F)
ACID RESISTANCE:
Required
Dielectric test, 2500 volts (rms), 60Hz
COLOR: In accordance with MIL-STD-1 04, Class 1 ; white preferred.
COLOR STRIPING OR BANDING DURABILITY: 250 cycles (500 strokes) (min), 500 grams weight
IDENTIFICATION DURABILITY: 1 25 cycles (250 strokes) (min), 500 grams weight
WIRE LENGTH REQUIREMENTS: Schedule B