ANSI AIIM MS15-2000 pdf download Dimensions and Operational Constraints for Single-Core Cartridge for I6 rnm Processed Microfilm
4.3 Film Speed in Operational Mode There shall be no detrimental film scratches or other film damage on a 3 meter (IO foot) strip of film that has been transported at maximum reader speed back and forth for 25 look-ups (50 passes). This should be compared against reference prints made prior to the test at the start, middle, and end of the film strip. Suitable testing and checking shall be performed to determine whether such scratching or film damage, if it occurs, is caused by the functioning of the cartridge or by the reader transport system.
4.4 Materials See also annex A.
4.4.1 Impact Strength The cartridge loaded with the equivalent of 30.m (100 feet) of nominal 0.1 3 mm (0.005 inch) thick film shall withstand the following test without rupture of the assembly and without impairment of use. Test: Drop the cartridge four times, once on a corner, once on an edge, and once on each face, from a height of 1 .22 m (4 feet) on a level flat steel surface.
4.4.2 Test Conditions Testing to determine compliance with impact strength shall be done under the following condi- tions: 50 percent f 1 5 percent relative humidity; 23 OC k 5 “C (73 O F f 9 “F). Samples shall be conditioned to this environment for 24 hours before testing.
4.4.3 Compatibility All materials of the cartridge shall be chosen so as not to cause loss of information on the film or loss of cartridge function (see annex A). Here firn refers to commercially available film at the time this standard was approved.
4.5 Lubrication The design shall be such that lubrication of the film or cartridge is not required by the user.
4.6 Permanent Markings Any marking permanently molded into the cartridge body, either inside or outside, shall be flush or below surfaces.
4.7 Labeling Areas provided for labeling shall be recessed and located such that the information on the label is not vulnerable to damage from handling and use.
4.8 Surface Finish The inside surface finish shall be free of any flashing or molding lines in the film path.