BS/EN 13445-2-2014 pdf download.Unfired pressure vessels Part 2 : Materials.
4.2.1.1 General
Where the behaviour of a material can be affected by manufacturing processes or operating conditions, to an extent that would adversely affect the safety or service life of the pressure vessel, this shall be taken into consideration when specifying material.
Adverse effects may arise from:
manufacturing processes: e.g. degree of cold forming and heat treatment:
operating conditions: e.g. hydrogen embrittlement, corrosion, scaling and ageing behaviour of the material
after cold forming.
4.2.1.2 Lamellar tearing
Where lamellar teanng due to the Joint design and loading needs to be addressed, steels shall be used which have improved deformation properties perpendicular to the surface and verified in accordance with EN 10164:2004.
NOTE For guidance see EN 1011.2.
4.2.2 Design temperature above 20 C
4.2.2.1 A material shall only be used for pressure parts within the range of temperatures for which the material properties required by EN 13445-3:2014 are defined in the technical specification for the material, If the technical delivery condition does not contain the specific material values required for the allowable temperature iN the values required in EN 13445-3:2014 for the design shall be determined by linear interpolation between the two adjacent values. Values shall not be rounded up.
For other than austenitic and austenitic-ferritic stainless steels, the specified value of R11 (R2) at room temperature (RT) may be used for temperatures less than or equal to 50 C. Interpolation between 50 ‘C and 100 ‘C shall be performed with the values of RT arid 100 ‘C and using 20 ‘C as the starting point for interpolation. Above 100 ‘C linear interpolation shall be performed between the tabulated values given in the table.
4.2.2.2 As the impact properties may be affected by long or frequent holding of the material at elevated temperatures, it is presupposed that the temperatures and periods of exposure to elevated temperatures be recorded for review during in-service inspection. The influence of such exposure upon the lifetime expectancy shall be estimated and recorded.
For operations such as drying and cleaning of pressure vessels, steels with specified low temperature properties but without elevated temperature 0,2 % proof strength values may however be used at elevated temperatures for drying and cleaning processes provided that the values of 0,2 % proof strength used in design calculations for elevated temperatures shall be obtained by multiplying the specified minimum yield strength values at 20 ‘C by the factor given in Table 4.2-1.
4.2.3 Prevention of brittle fracture
The requirements in Annex B shall apply.
4.2.4 DesIgn properties in the creep range
4.2.4.1 Creep properties of base material
For interpolation and extrapolation of creep properties given in the materials standard, see EN 13445-3:2014, Clause 19.
When creep properties are not available from a materials standard, they shall be determined using
EN ISO 204:2009.
4.2.4.2 Creep properties of weldments
Creep properties of weld joints subjected to stresses normal to the weld can differ significantly from those of the base material.
For the design of vessels in the creep range, this is taken into account in EN 13445-3:2014 by making use of a weld creep strength reduction factor z obtained from tests on weidments. If no data are available, a default value of z is used.
An acceptable method to determine z, by cross-weld tests is given In Annex C (see also (1 7’]).
4.2.5 Specific requirements for steels for fasteners Fasteners include bolts, studs and nuts.
Free cutting steel shall not be used. Bolting made of carbon steel or Ni alloy lemtic steel with > 3,5 % nickel shall not be used above 300 C.
The specified minimum tensile strength of bar material of ferntic and martensitic steel for bolts shall not exceed 1 000 MPa. The minimum elongation of bar material after fracture shall be at least A = 14 %.
Impact requirements for territic and martensitic steels are specified in B.2.2.4.
Boll material with a design temperature below -160 °C shall be impact tested at -196 °C.
Hydrogen embnttlement, fatigue or relaxation properties shall be taken into account where appropriate.BS/EN 13445-2-2014 pdf download.

                                           Related Information                                             Download
PS:Thank you for your support!
BS EN 12607-3-2000 pdf download BS Standards

BS EN 12607-3-2000 pdf download

BS EN 12607-3-2000 pdf download.Methods of test for petroleum and its products — BS 2000-460.3: Bitumen and bituminous binders — Determination of the resistance to hardening under the influence of heat and air — Part 3: RFT...
Read More
EN 12329-2000 pdf download BS Standards

EN 12329-2000 pdf download

BS EN 12329-2000 pdf download.Corrosion protection of metals — Electrodeposited coatings of zinc with supplementary treatment on iron or steel. This BS EN 12329 specifies requirements for electrodeposited coatings of zinc on iron or steel witt supplementary...
Read More
BS EN 1430-2000 pdf download BS Standards

BS EN 1430-2000 pdf download

BS EN 1430-2000 pdf download.Methods of test for petroleum and its products — BS 2000-292:Bitumen and bituminous binders — Determination of particle polarity of bitumen emulsions (Identical with IP 292-2000). This BS EN 1430 specifies a method...
Read More

LEAVE A REPLY

Anonymous netizen Fill in information